Verbatim 3d printer filament abs 2.85mm, 152m, 1kg black (old pn 55018)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 230 - 240 °C Material Net Weight 1.00 kg Color black Filament Length 70 m (for 2.85mm thickness) 404 m (for 1.75mm thickness) Density 1.05 g/cm3 Tensile Yield 48 MPa Flexural Strength 76 MPa Flexural Modulus 2.2 GPa Impact Strength (Charpy) 20 KJ/m2 Heat Distortion Temperature 98 °C Molding Shrinkage 0.3 – 0.7% (patro.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 230 - 240 °C Material Net Weight 1.00 kg Color silver/metal grey Filament Length 70 m (for 2.85mm thickness), 404 m (for 1.75mm thickness) Density 1.05 g/cm3 Tensile Yield 48 MPa Flexural Strength 76 MPa Flexural Modulus 2.2 GPa Impact Strength (Charpy) 20 KJ/m2 Heat Distortion Temperature (HDT) 98 °C Molding Shrinkage 0.3 – 0.7% (patro.cz)

TECHNICAL SPECIFICATIONS GENERAL Size 1.75 mm Diam. tolerance ±0.05 mm Length 396 m MATERIAL PROPERTIES Density 1.05 g/cm (ISO 1183) Viscat softening temperature 104 °C (ISO 306) Flexural strength 76 MPa (ISO 178) Flexural modulus 220 Mpa (ISO 178) Impact strength - Charpy method 23°C 21 kJ/m2 (ISO 179) Tensile strength 47 Mpa (ISO 527) Tensile elongation 30% (ISO 527) RECOMMENDED PRINTER SET UP Extrusion temperature 250±10 °C Bed temperature 90°C Printing speed 30 mm/s (patro.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 230 - 240 °C Material Net Weight 1.00 kg Color black Filament Length 70 m (for 2.85mm thickness) 404 m (for 1.75mm thickness) Density 1.05 g/cm3 Tensile Yield 48 MPa Flexural Strength 76 MPa Flexural Modulus 2.2 GPa Impact Strength (Charpy) 20 KJ/m2 Heat Distortion Temperature 98 °C Molding Shrinkage 0.3 – 0.7% . (cdrmarket.cz)

ABS Filament High performance Acrylonitrile Butadiene Styrene (ABS) for material extrusion (ME) High rigidity, high gloss, medium impact strength Resistant to grease Good post-printing workability Strong odour during printing Main applications: Concept modelling for building, electrical, automotive industry etc. Non-critical parts such as enclosures. TECHNICAL SPECIFICATIONS Size 2.85mm ± 0.09mm Material Net Weight 1.00 kg Color white Filament Length 149 m Density 1.05 g/cm3 Viscat softening temperature 104°C Flexural Strength 76 MPa Flexural Modulus 2.2 GPa Impact Strength (Charpy method 23°C) 21 kJ/m2 Tensile strength 47 Mpa Tensile elongation 30% RECOMMENDED PRINTER SET UP Extrusion temperature 250±10°C Bed temperature 90 °C Printing speed 30 mm/s (patro.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 200 - 220 °C Material Net Weight 1.00 kg Color red Filament Length 119 m (for 2.85 thickness), 334 m (for 1.75mm thickness) Density 1.24 g/cm3 Melting Point 155 - 170 °C Tensile strength 15 - 21 kpsi Tensile modulus 500 - 550 kpsi (patro.cz)

Features High performance Polyactic Acid (PLA) for material extrusion (ME) Biopolymer derived from plants Good post-printing workability Odourless Main applications: Concept modelling for food packaging, transport containers, medical/hygienic products, housings, education. TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 200 - 220 °C Material Net Weight 1.00 kg Color blue Filament Length 126 m (for 2.85 thickness) Density 1.24 g/cm3 Melt flow rate (210°C, 21.2N) 8.1 g/10min Glass transition temperature 58 °C Melt temperature 168 °C Tensile strength 63 Mpa Tensile elongation 4% (patro.cz)

Features High performance Polyactic Acid (PLA) for material extrusion (ME) Biopolymer derived from plants Good post-printing workability Odourless Main applications: Concept modelling for food packaging, transport containers, medical/hygienic products, housings, education. TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 200 - 220 °C Material Net Weight 1.00 kg Color blue Filament Length 126 m (for 2.85 thickness) Density 1.24 g/cm3 Melt flow rate (210°C, 21.2N) 8.1 g/10min Glass transition temperature 58 °C Melt temperature 168 °C Tensile strength 63 Mpa Tensile elongation 4% (patro.cz)

Filament Verbatim PLA 2.85mm 1kg - strieborná PLA je ľahko tlačiteľné vlákno vyrobené z obnoviteľných rastlinných zdrojov. Materiál Verbatim PLA sa vyrába podľa špeciálnej receptúry s vysokou štandardnou kontrolou kvality. Je bez zápachu a má dobrú spracovateľnosť po tlači, čo z neho robí vynikajúci univerzálny materiál na širokú škálu aplikácií vrátane modelovania konceptov a vzdelávania. Funkcie Vysokoúčinná kyselina polymliečna (PLA) na vytláčanie materiálov Biopolymér získaný z rastlín Dobrá spracovateľnosť po tlači Bez zápachu Hlavné aplikácie: modelovanie konceptov pre obaly na potraviny, prepravné nádoby, lekárske/hygienické výrobky, kryty. Vzdelanie. TECHNICKÉ ŠPECIFIKÁCIE Presnosť priemeru 2.85 ± 0.05 mm Procesná teplota 200-220 °C Čistá hmotnosť materiálu 1.00 kg Hrubá hmotnosť materiálu 1.50 kg Dĺžka vlákna 126 m Teplota topenia 168 °C Hustota 1.24 g/cm3 Teplota sklovitého prechodu 58 °C Medz pevnosti v ťahu 63 MPa Predĺženie v ťahu 4 % Prietok taveniny (190 °C, 21.2N) 3.0 g/(10 minút) Prietok taveniny (210 °C, 21.2N) 8.1 g/(10 minút) ROZMERY CIEVKY Priemer cievky 200 mm Hĺbka cievky 72 mm Priemer náboja 102 mm Priemer otvoru v náboji 51 mm ODPORÚČANÉ NASTAVENIE TLAČIARNE Teplota vytláčania 210±10 °C Teplota lôžka 60 °C Rýchlosť tlače 30 mm/s . (patro.cz)

TECHNICAL SPECIFICATIONS Diameter 2.85 mm ± 0.10 mm Roundness >95% RAL 9005 Weight 500 g Color black MATERIAL PROPERTIES Density 1.31 g/cm3 (Test method: ISO 1183) MVR 230°C/2.16 kg 10 cm3/10min (ISO 1133) MFR 230°C/2.16 kg 13 gr/10 min (Test method: ISO 1133) Elongation at break 130% (Test method: ISO 527) Tensile strength 64 MPa (Test method: ISO 527) Tensile modulus 2300MPa (Test method: ISO 527) Flexural modulus 2100MPa (Test method: ISO 178) Flexural strength 94 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 9 kJ/m2 (Test method: ISO 179) Moisture absorption 0.2% (Test method: MCC Method) Coefficient of linear thermal expansion (-20 80°C) 7.3E-05 (Test method: ISO 11359-2) Heat deflection temperature 1.80 MPa 82°C (Test metod: ISO 75-1) Transparency 2% (Test method: ISO 13468) RECOMMENDED PRINTER SET UP Extrusion temperature 225 - 245°C Melting temperature 235°C Bed temperature 85°C Printing speed 50 mm/s Fan speed (can be changed to 0% is the model is warping) 10% (patro.cz)

TECHNICAL SPECIFICATIONS Diameter Tolerance ± 0.05 mm Extrusion temperature 200 - 240 °C Material Net Weight 500 g Color transparent Filament Length 1.75 mm - 233 m, 2.85 mm - 88 m Density 0.89 g/ cm3 Flexural Modulus 350 MPa Flexural Strength 14 MPa Tensile Strength 14 MPa Impact Strength (Charpy) 10 kJ/m2 Tensile Elongation > 200 % Durometer Hardness Durometer Hardness Vicat softening temperature 115 °C Printing speed 30mm/s High quality Polypropylene (PP) filamentTo be used in widely available Fused Fabrication Filament (FFF) printersVery good heat resistanceSuitable for food packaging, medical applications, IT equipment and other applications that require softness and heat resistanceA long-standing staple of plastic containers, Polypropylene (PP) 3D print filament enables you to create durable, flexible, transparent, heat- and chemical-resistant containers for food packaging, medical equipment, IT kit and other appliances.It requires a heated print bed of around 100°C and is ideal for objects that require softness, transparency and heat resistance. (patro.cz)

TECHNICAL SPECIFICATIONS Diameter 1.75 mm ± 0.05 mm Roundness >95% RAL 9003 Weight 500 g Color white MATERIAL PROPERTIES Density 1.31 g/cm3 (Test method: ISO 1183) MVR 230°C/2.16 kg 10 cm3/10min (ISO 1133) MFR 230°C/2.16 kg 13 gr/10 min (Test method: ISO 1133) Elongation at break 130% (Test method: ISO 527) Tensile strength 64 MPa (Test method: ISO 527) Tensile modulus 2300MPa (Test method: ISO 527) Flexural modulus 2100MPa (Test method: ISO 178) Flexural strength 94 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 9 kJ/m2 (Test method: ISO 179) Moisture absorption 0.2% (Test method: MCC Method) Coefficient of linear thermal expansion (-20 80°C) 7.3E-05 (Test method: ISO 11359-2) Heat deflection temperature 1.80 MPa 82°C (Test metod: ISO 75-1) Transparency 2% (Test method: ISO 13468) RECOMMENDED PRINTER SET UP Extrusion temperature 225 - 245°C Melting temperature 235°C Bed temperature 85°C Printing speed 50 mm/s Fan speed (can be changed to 0% is the model is warping) 10% (patro.cz)

Vlákno Verbatim BVOH 1.75 mm - priehľadné Vysokokvalitný nosný materiál rozpustný vo vode, ktorý sa môže používať s množstvom rôznych polymérov a ľahko sa rozpúšťa v studenej vode. Tento ekologický materiál poskytuje podporu pri tlači objektov s presahmi alebo obzvlášť zložitých štruktúr. Spoločnosť Verbatim BVOH štandardne dodržiava najprísnejšie kontroly kvality, čím zabezpečuje vynikajúce vlastnosti pri vytváraní vrstiev a priľnavosť. Funkcie Butendiol-vinylalkoholový kopolymér (BVOH) na vytláčanie materiálov Nosný materiál rozpustný vo vode Odpad možno likvidovať spolu s odpadovými vodami z domácností** Vynikajúce lepidlo na tvorbu vrstiev, emulgátor, lepidlo Najlepšie v kombinácii s materiálmi ABS, PLA a PET Citlivosť na svetlo a UV žiarenie Vysoká rozpustnosť Hlavné aplikácie: Podporný materiál pre vlákna, tlačové projekty s presahmi alebo zložitými objektmi **>20-násobok hmotnosti vody k tomuto materiálu potrebnej na likvidáciu (t. j.e >20cc vody na 1g BVOH) s maximálnym množstvom 2kg BVOH denne. Ak sa má denne použiť viac BVOH, bude potrebné profesionálne čistenie organických odpadových vôd. TECHNICKÉ ŠPECIFIKÁCIE Presnosť priemeru 1.75 mm ± 0.07 mm Čistá hmotnosť materiálu 0.5 kg Dĺžka vlákna 182 m Teplota topenia 176 °C Prietok taveniny pri 230 °C, 21.1N 7.5 g/(10 minút) Hustota 1.14 g/cm3 Teplota mäknutia Viscat 92 °C Teplota sklovitého prechodu 68 °C Pevnosť v ohybe 71 MPa Modul pružnosti v ohybe 2900 MPa Pevnosť v ťahu 45 MPa Pružnosť v ťahu 9.0% ROZMERY CIEVKY Priemer cievky 200 mm Hĺbka cievky 72 mm Priemer náboja 102 mm Priemer otvoru v náboji 51 mm ODPORÚČANÉ NASTAVENIE TLAČIARNE Teplota vytláčania 210±10 °C Teplota lôžka 60 °C Rýchlosť tlače 30 mm/s . (patro.cz)

Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 2.85 mm ± 0.10 mm Roundness >95% RAL N/A Weight 1000 g Color transparent MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) (patro.cz)

Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 2.85 mm ± 0.10 mm Roundness >95% RAL 5002 Weight 1000 g Color blue MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) (patro.cz)

TECHNICAL SPECIFICATIONS Diameter 2.85 mm ± 0.10 mm Roundness >95% RAL 9003 Weight 500 g Color white MATERIAL PROPERTIES Density 1.31 g/cm3 (Test method: ISO 1183) MVR 230°C/2.16 kg 10 cm3/10min (ISO 1133) MFR 230°C/2.16 kg 13 gr/10 min (Test method: ISO 1133) Elongation at break 130% (Test method: ISO 527) Tensile strength 64 MPa (Test method: ISO 527) Tensile modulus 2300MPa (Test method: ISO 527) Flexural modulus 2100MPa (Test method: ISO 178) Flexural strength 94 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 9 kJ/m2 (Test method: ISO 179) Moisture absaorption 0.2% (Test method: MCC Method) Coefficient of linear thermal expansion (-20 80°C) 7.3E-05 (Test method: ISO 11359-2) Heat deflection temperature 1.80 MPa 82°C (Test metod: ISO 75-1) Transparency 2% (Test method: ISO 13468) RECOMMENDED PRINTER SET UP Extrusion temperature 225 - 245°C Melting temperature 235°C Bed temperature 85°C Printing speed 50 mm/s Fan speed (can be changed to 0% is the model is warping) 10% (patro.cz)

Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 2.85 mm ± 0.10 mm Roundness >95% RAL 3020 Weight 1000 g Color red MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) (patro.cz)

Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 1.75 mm ± 0.05 mm Roundness >95% RAL 3020 Weight 1000 g Color red MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) (patro.cz)

TECHNICAL SPECIFICATIONS Diameter 1.75 mm ± 0.05 mm Roundness >95% RAL N/A Weight 500 g Color transparent MATERIAL PROPERTIES Density 1.31 g/cm3 (Test method: ISO 1183) MVR 230°C/2.16 kg 10 cm3/10min (ISO 1133) MFR 230°C/2.16 kg 13 gr/10 min (Test method: ISO 1133) Elongation at break 130% (Test method: ISO 527) Tensile strength 64 MPa (Test method: ISO 527) Tensile modulus 2300MPa (Test method: ISO 527) Flexural modulus 2100MPa (Test method: ISO 178) Flexural strength 94 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 9 kJ/m2 (Test method: ISO 179) Moisture absorption 0.2% (Test method: MCC Method) Coefficient of linear thermal expansion (-20 80°C) 7.3E-05 (Test method: ISO 11359-2) Heat deflection temperature 1.80 MPa 82°C (Test metod: ISO 75-1) Transparency 2% (Test method: ISO 13468) RECOMMENDED PRINTER SET UP Extrusion temperature 225 - 245°C Melting temperature 235°C Bed temperature 85°C Printing speed 50 mm/s Fan speed (can be changed to 0% is the model is warping) 10% (patro.cz)

Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 2.85 mm ± 0.10 mm Roundness >95% RAL - Weight 1000 g Color blue transparent MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) (patro.cz)

Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 1.75 mm ± 0.05 mm Roundness >95% RAL - Weight 1000 g Color red transparent MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) (patro.cz)

Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 1.75 mm ± 0.05 mm Roundness >95% RAL - Weight 1000 g Color green transparent MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) (patro.cz)

Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 1.75 mm ± 0.05 mm Roundness >95% RAL - Weight 1000 g Color blue transparent MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) (patro.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 230 - 240 °C Material Net Weight 1.00 kg Color silver/metal grey Filament Length 70 m (for 2.85mm thickness), 404 m (for 1.75mm thickness) Density 1.05 g/cm3 Tensile Yield 48 MPa Flexural Strength 76 MPa Flexural Modulus 2.2 GPa Impact Strength (Charpy) 20 KJ/m2 Heat Distortion Temperature (HDT) 98 °C Molding Shrinkage 0.3 – 0.7% . (cdrmarket.cz)

VERBATIM 3D Printer Filament ABS 1,75mm (2019), černá Vysoce odolný akrolynitrilbutadienstyren (ABS) pro vytlačování materiálu Materiál se vyznačuje vysokou tuhostí, vysokým leskem a střední odolností proti nárazům Odolný vůči tukům a mazivům Dobrá následná opracovatelnost (post processing) Silný zápach během tisku Hlavní aplikace: Protypové modely pro stavební, elektrotechnický, automobilový průmysl atd. Mechanicky méně namáhané součásti TECHNICKÉ SPECIFIKACE Přesnost průměru 1.75 ± 0.05 mm Čistá hmotnost 1,00 kg Hrubá hmotnost 1,5 Délka vlákna 396 m Hustota 1,05 g/cm3 Flexural strength 76 MPa Flexural modulus 2200 MPa Impact strength (Charpy) 21 KJ/m2 Molding shrinkage 0.3 – 0.7 % Mez v kluzu (JIS K 7113) 47 MPa Prodloužení (JIS K 7113) 30 % Průměr cívky 200 mm Hloubka cívky 72 mm Průměr náboje 102 mm Průměr otvoru náboje 51 mm Doporučené Nastavení Tiskárny Teplota vytlačování: 250±10 °CTeplota podložky: 90 °CRychlost tisku: 30 mm/s . (cdrmarket.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 200 - 220 °C Material Net Weight 1.00 kg Color red Filament Length 119 m (for 2.85 thickness), 334 m (for 1.75mm thickness) Density 1.24 g/cm3 Tensile Strength 15-21 kpsi Tensile Modulus 500 - 550 kpsi Melting Point 155 - 170 °C . (cdrmarket.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 200 - 220 °C Material Net Weight 1.00 kg Color white Filament Length 119 m (for 2.85 thickness), 334 m (for 1.75mm thickness) Density 1.24 g/cm3 Tensile Strength 15-21 kpsi Tensile Modulus 500 - 550 kpsi Melting Point 155 - 170 °C . (cdrmarket.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 200 - 220 °C Material Net Weight 1.00 kg Color blue Filament Length 119 m (for 2.85 thickness), 334 m (for 1.75mm thickness) Density 1.24 g/cm3 Tensile Strength 15-21 kpsi Tensile Modulus 500 - 550 kpsi Melting Point 155 - 170 °C . (cdrmarket.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 200 - 220 °C Material Net Weight 1.00 kg Color natural transparent Filament Length 119 m (for 2.85 thickness), 334 m (for 1.75mm thickness) Density 1.24 g/cm3 Tensile Strength 15 - 21 kpsi Tensile Modulus 500 - 550 kpsi Melting Point 155 - 170 °C . (cdrmarket.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 200 - 220 °C Material Net Weight 1.00 kg Color transparent natural Filament Length 119 m (for 2.85 thickness), 334 m (for 1.75mm thickness) Density 1.24 g/cm3 Melting Point 155 - 170 °C Tensile strength 15 - 21 kpsi Tensile modulus 500 - 550 kpsi . (cdrmarket.cz)

TECHNICAL SPECIFICATIONS GENERAL Size 1.75 mm Diam. tolerance ±0.05 mm Length 396 m MATERIAL PROPERTIES Density 1.05 g/cm (ISO 1183) Viscat softening temperature 104 °C (ISO 306) Flexural strength 76 MPa (ISO 178) Flexural modulus 220 Mpa (ISO 178) Impact strength - Charpy method 23°C 21 kJ/m2 (ISO 179) Tensile strength 47 Mpa (ISO 527) Tensile elongation 30% (ISO 527) RECOMMENDED PRINTER SET UP Extrusion temperature 250±10 °C Bed temperature 90°C Printing speed 30 mm/s . (cdrmarket.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 200 - 220 °C Material Net Weight 1.00 kg Color green Filament Length 119 m (for 2.85 thickness), 334 m (for 1.75mm thickness) Density 1.24 g/cm3 Tensile Strength 15-21 kpsi Tensile Modulus 500 - 550 kpsi Melting Point 155 - 170 °C . (cdrmarket.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 230 - 240 °C Material Net Weight 1.00 kg Color black Filament Length 70 m (for 2.85mm thickness), 404 m (for 1.75mm thickness) Density 1.05 g/cm3 Tensile Yield 48 MPa Flexural Strength 76 MPa Flexural Modulus 2.2 GPa Impact Strength (Charpy) 20 KJ/m2 Heat Distortion Temperature (HDT) 98 °C Molding Shrinkage 0.3 – 0.7% . (cdrmarket.cz)

ABS Filament High performance Acrylonitrile Butadiene Styrene (ABS) for material extrusion (ME) High rigidity, high gloss, medium impact strength Resistant to grease Good post-printing workability Strong odour during printing Main applications: Concept modelling for building, electrical, automotive industry etc. Non-critical parts such as enclosures. TECHNICAL SPECIFICATIONS Size 2.85mm ± 0.09mm Material Net Weight 1.00 kg Color white Filament Length 149 m Density 1.05 g/cm3 Viscat softening temperature 104°C Flexural Strength 76 MPa Flexural Modulus 2.2 GPa Impact Strength (Charpy method 23°C) 21 kJ/m2 Tensile strength 47 Mpa Tensile elongation 30% RECOMMENDED PRINTER SET UP Extrusion temperature 250±10°C Bed temperature 90 °C Printing speed 30 mm/s . (cdrmarket.cz)

TECHNICAL SPECIFICATIONS GENERAL Size 1.75 mm Diam. tolerance ±0.05 mm Length 396 m MATERIAL PROPERTIES Density 1.05 g/cm (ISO 1183) Viscat softening temperature 104 °C (ISO 306) Flexural strength 76 MPa (ISO 178) Flexural modulus 220 Mpa (ISO 178) Impact strength - Charpy method 23°C 21 kJ/m2 (ISO 179) Tensile strength 47 Mpa (ISO 527) Tensile elongation 30% (ISO 527) RECOMMENDED PRINTER SET UP Extrusion temperature 250±10 °C Bed temperature 90°C Printing speed 30 mm/s . (cdrmarket.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 230 - 240 °C Material Net Weight 1.00 kg Color transparent Filament Length 70 m (for 2.85mm thickness), 404 m (for 1.75mm thickness) Density 1.08 g/cm3 Tensile Yield 42 MPa Flexural Strength 61 MPa Flexural Modulus 2.1 GPa Impact Strength (Charpy) 12 KJ/m2 Heat Distortion Temperature (HDT) 99 °C Molding Shrinkage N/A . (cdrmarket.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 230 - 240 °C Material Net Weight 1.00 kg Color transparent Filament Length 70 m (for 2.85mm thickness), 404 m (for 1.75mm thickness) Density 1.08 g/cm3 Tensile Yield 42 MPa Flexural Strength 61 MPa Flexural Modulus 2.1 GPa Impact Strength (Charpy) 12 KJ/m2 Heat Distortion Temperature (HDT) 99 °C Molding Shrinkage N/A . (cdrmarket.cz)

Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 2.85 mm ± 0.10 mm Roundness >95% RAL - Weight 1000 g Color green transparent MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) (patro.cz)

Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 2.85 mm ± 0.10 mm Roundness >95% RAL - Weight 1000 g Color red transparent MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) (patro.cz)

TECHNICAL SPECIFICATIONS GENERAL Size 1.75 mm Diam. tolerance ±0.05 mm Length 396 m MATERIAL PROPERTIES Density 1.05 g/cm (ISO 1183) Viscat softening temperature 104 °C (ISO 306) Flexural strength 76 MPa (ISO 178) Flexural modulus 220 Mpa (ISO 178) Impact strength - Charpy method 23°C 21 kJ/m2 (ISO 179) Tensile strength 47 Mpa (ISO 527) Tensile elongation 30% (ISO 527) RECOMMENDED PRINTER SET UP Extrusion temperature 250±10 °C Bed temperature 90°C Printing speed 30 mm/s (patro.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 200 - 220 °C Material Net Weight 1.00 kg Color silver/metal grey Filament Length 119 m (for 2.85 thickness), 334 m (for 1.75mm thickness) Density 1.24 g/cm3 Melting Point 155 - 170 °C Tensile strength 15 - 21 kpsi Tensile modulus 500 - 550 kpsi . (cdrmarket.cz)

TECHNICAL SPECIFICATIONS Diameter accuracy 2.90 mm ± 0.03 mm 1.75 mm ± 0.02 mm Extrusion temperature 200 - 220 °C Material Net Weight 1.00 kg Color black Filament Length 119 m (for 2.85 thickness), 334 m (for 1.75mm thickness) Density 1.24 g/cm3 Tensile Strength 15-21 kpsi Tensile Modulus 500 – 550 kpsi Melting Point 155 - 170 °C . (cdrmarket.cz)

Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 1.75 mm ± 0.05 mm Roundness >95% RAL 9017 Weight 1000 g Color black MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) . (cdrmarket.cz)

Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 2.85 mm ± 0.10 mm Roundness >95% RAL 9017 Weight 1000 g Color black MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) . (cdrmarket.cz)

Verbatim PLA Filament 2.85mm 1kg - Silver PLA is an easy-to-print filament made of renewable plant-based resources. Verbatim PLA is made to a special recipe with high quality controls as standard. It is odourless with good post-printing workability, making it a wonderful all-purpose material for a wide range of applications including concept modelling and education. Features High performance Polyactic Acid (PLA) for material extrusion Biopolymer derived from plants Good post-printing workability Odourless Main applications: Concept modelling for food packaging, transport containers, medical/hygienic products, housings. Education. TECHNICAL SPECIFICATIONS Diameter accuracy 2.85 ± 0.05 mm Process temperature 200-220 °C Material net weight 1.00 kg Material gross weight 1.50 kg Filament length 126 m Melt temperature 168 °C Density 1.24 g/cm3 Glass transition temperature 58 °C Tensile yield 63 MPa Tensile elongation 4 % Melt Flow Rate (190 °C, 21.2N) 3.0 g/(10 minutes) Melt Flow Rate (210 °C, 21.2N) 8.1 g/(10 minutes) SPOOL DIMENSIONS Spool diameter 200 mm Spool depth 72 mm Hub diameter 102 mm Hub hole diameter 51 mm RECOMMENDED PRINTER SET UP Extrusion temperature 210±10 °C Bed temperature 60 °C Printing speed 30 mm/s . (cdrmarket.cz)

Verbatim PLA Filament 2.85mm 1kg - White PLA is an easy-to-print filament made of renewable plant-based resources. Verbatim PLA is made to a special recipe with high quality controls as standard. It is odourless with good post-printing workability, making it a wonderful all-purpose material for a wide range of applications including concept modelling and education. Features High performance Polyactic Acid (PLA) for material extrusion Biopolymer derived from plants Good post-printing workability Odourless Main applications: Concept modelling for food packaging, transport containers, medical/hygienic products, housings. Education. TECHNICAL SPECIFICATIONS Diameter accuracy 2.85 ± 0.05 mm Process temperature 200-220 °C Material net weight 1.00 kg Material gross weight 1.50 kg Filament length 126 m Melt temperature 168 °C Density 1.24 g/cm3 Glass transition temperature 58 °C Tensile yield 63 MPa Tensile elongation 4 % Melt Flow Rate (190 °C, 21.2N) 3.0 g/(10 minutes) Melt Flow Rate (210 °C, 21.2N) 8.1 g/(10 minutes) SPOOL DIMENSIONS Spool diameter 200 mm Spool depth 72 mm Hub diameter 102 mm Hub hole diameter 51 mm RECOMMENDED PRINTER SET UP Extrusion temperature 210±10 °C Bed temperature 60 °C Printing speed 30 mm/s . (cdrmarket.cz)

Filament - materiál ABS metalický, průměr 1,75 mm s tolerancí 0,05 mm, hmotnost 1 kg, vhodná teplota tisku až 250 °C, teplota podložky 90°C, doporučená rychlost tisku od 40 mm/s do 60 mm/s Provozujete 3D tiskárnu? Pak si doplňte zásobu tiskových materiálů o vysoce odolné vlákno Verbatim ABS. Materiál se vyznačuje vysokou tuhostí, vysokým leskem a střední odolností proti nárazům. Také je odolný vůči tukům a mazivům a výsledné 3D tisky lze i následně opracovat (post processing) do dokonalosti. Skvěle se proto hodí pro prototypy modelů a pro mechanicky méně namáhané součásti v elektrotechnickém či automobilovém průmyslu. Vlákno je dodáváno navinuté na cívce.Klíčové vlastnosti ABS struny Verbatim stříbrnéVysoce odolný ABS pro 3D tisk technologií FFFVysoká tuhost, vysoký lesk a střední odolnost proti nárazůmOdolný vůči tukům a mazivůmVynikající následná opracovatelnost (post processing)Silný zápach během tiskuDodáváno navinuté na cívce (alza.cz)

Filament - materiál ABS, průměr 1,75 mm s tolerancí 0,05 mm, hmotnost 1 kg, vhodná teplota tisku až 250 °C, teplota podložky 90°C, doporučená rychlost tisku od 40 mm/s do 60 mm/s Provozujete 3D tiskárnu? Pak si doplňte zásobu tiskových materiálů o vysoce odolné vlákno Verbatim ABS. Materiál se vyznačuje vysokou tuhostí, vysokým leskem a střední odolností proti nárazům. Také je odolný vůči tukům a mazivům a výsledné 3D tisky lze i následně opracovat (post processing) do dokonalosti. Skvěle se proto hodí pro prototypy modelů a pro mechanicky méně namáhané součásti v elektrotechnickém či automobilovém průmyslu. Vlákno je dodáváno navinuté na cívce.Klíčové vlastnosti ABS struny Verbatim černéVysoce odolný ABS pro 3D tisk technologií FFFVysoká tuhost, vysoký lesk a střední odolnost proti nárazůmOdolný vůči tukům a mazivůmVynikající následná opracovatelnost (post processing)Silný zápach během tiskuDodáváno navinuté na cívce (alza.cz)

Filament - materiál ABS, průměr 2,85 mm s tolerancí 0,05 mm, hmotnost 1 kg, vhodná teplota tisku až 250 °C, teplota podložky 90°C, doporučená rychlost tisku od 40 mm/s do 60 mm/s Provozujete 3D tiskárnu? Pak si doplňte zásobu tiskových materiálů o vysoce odolné 2,85mm vlákno Verbatim ABS. Materiál se vyznačuje vysokou tuhostí, vysokým leskem a střední odolností proti nárazům. Také je odolný vůči tukům a mazivům a výsledné 3D tisky lze i následně opracovat (post processing) do dokonalosti. Skvěle se proto hodí pro prototypy modelů a pro mechanicky méně namáhané součásti v elektrotechnickém či automobilovém průmyslu. Vlákno je dodáváno navinuté na cívce.Klíčové vlastnosti 2,85mm ABS struny Verbatim černéVysoce odolný ABS pro 3D tisk technologií FFFVysoká tuhost, vysoký lesk a střední odolnost proti nárazůmOdolný vůči tukům a mazivůmVynikající následná opracovatelnost (post processing)Silný zápach během tiskuDodáváno navinuté na cívce (alza.cz)

Filament - materiál ABS, průměr 1,75 mm s tolerancí 0,05 mm, hmotnost 1 kg, vhodná teplota tisku až 250 °C, teplota podložky 90°C, doporučená rychlost tisku od 40 mm/s do 60 mm/s Provozujete 3D tiskárnu? Pak si doplňte zásobu tiskových materiálů o vysoce odolné vlákno Verbatim ABS. Materiál se vyznačuje vysokou tuhostí, vysokým leskem a střední odolností proti nárazům. Také je odolný vůči tukům a mazivům a výsledné 3D tisky lze i následně opracovat (post processing) do dokonalosti. Skvěle se proto hodí pro prototypy modelů a pro mechanicky méně namáhané součásti v elektrotechnickém či automobilovém průmyslu. Vlákno je dodáváno navinuté na cívce.Klíčové vlastnosti ABS struny Verbatim modréVysoce odolný ABS pro 3D tisk technologií FFFVysoká tuhost, vysoký lesk a střední odolnost proti nárazůmOdolný vůči tukům a mazivůmVynikající následná opracovatelnost (post processing)Silný zápach během tiskuDodáváno navinuté na cívce (alza.cz)